UTEC®
UTEC6540G
UTEC6540Gis an Ultra High Molecular Weight Polyethylene with a molecular weight greater than 10 times higher than High Density Polyethylene (HDPE) resins. This extremely highmolecular weight yields several unique properties to this polymer such as high abrasion resistance, impact strength, and because it is a self-lubricating material, a low coefficient of friction.
Application: Technical parts RAM extruded and compression molded sheets, rods and profiles.;
Behavior
Volume Resistivity
> 10<sup>14</sup>
ohm.cm
ASTM D257
Surface Resistivity
> 10<sup>12</sup>
ohm
ASTM D257
Tensile Strength at Yield
≥ 17
MPa
ASTM D638 ISO 527
Tensile Strength at Break
> 30
MPa
ASTM D638 ISO 527
More Details
Method
Units
Value
Ultimate Elongation
ASTM D638 ISO 527
%
> 350
Double Notch Charpy Impact Strength
ISO 11542-2
KJ/m<sup>2</sup>
> 100
Shore D Hardness
ASTM D2240 ISO 868
-
64
Shore D Hardness (15 sec)
ASTM D2240 ISO 868
-
> 58
Intrinsic Viscosity
ASTM D4020
dL/g
28
Average Molecular Weight
Internal
g/mol
8.0 x 10<sup>6</sup>
Density
ASTM D792
g/cm³
0.925
Bulk Density
ASTM D1895
g/cm³
0.45
Average Particle Size Dp50
LaserLightScattering
µm
255
Melt Temperature
ASTM D3418
ºC
133