I'm green bio-basedTM Polyethylene - High Density
Share
SHE150
SHE150 Braskem Logo

SHE150 resin is a High Density Polyethylene that has been specially designed for monofilament extrusion process and provides a good balance of processability, spinnability, knotting strength as well as a very low gels amount. It can also be blended with LLDPE to improve blown film stiffness. It contains processing aid and antioxidant additives. The minimum biobased carbon content of this grade is 94%, determined according to ASTM D6866.

Process: Extrusion of Monofilaments;

Application: Film;Raschel;Ropes;Shading nets;

Behavior Behavior
Melt Flow Rate (190°C/2.16kg)
1 g/10 min D 1238
Density
0.948 g/cm³ D 792
Density
0.948 g/cm³ ISO 1183-1
Melt Flow Rate (190°C/2,16 kg)
1 g/10 min ISO 1133
More Details
Method
Units
Value
Tensile Strength at Yield (b)
 ISO 527
 MPa
 27
Elongation at Yield (b)
 ISO 527
 %
 10
Tensile Strength at Break (b)
 ISO 527
 MPa
 31
Elongation at Break (b)
 ISO 527
 %
 2200
Flexural Modulus Chord 0.05-0.25 % (b)
 ISO 178
 MPa
 1071
Izod Impact Strength 23 °C (b)
 ISO 180
 kJ/m²
 14
Vicat Softening Temperature at 10 N (a)
 ISO 306
 °C
 129
Deflection Temperature Under Load at 0.455 MPa (b)
 ISO 75
 °C
 63
Tensile Strength at Yield (a)
 D 638
 MPa
 28
Tensile Strength at Break (a)
 D 638
 MPa
 40
Flexural Modulus - 2% Secant (b)
 D 2240
 MPa
 1280
Hardness (c)
 D 2240
 -
 62
Deflection Temperature under Load at 0.455 MPa (b)
 D 648
 °C
 76
Vicat Softening Temperature at 10 N (b)
 D 1525
 °C
 128