I'm green bio-basedTM Polyethylene - High Density
Share
SHC7260
SHC7260 Braskem Logo

SHC7260 is a high-density polyethylene, developed for the injection molding which presents high hardness and stiffness, besides low tendency to warpage. Organoleptic properties are suitable for water caps applications. The minimum biobased carbon content of this grade is 94%, determined according to ASTM D6866.

Process: Injection molding;

Application: Caps for non-carbonated or low carbonated soft drinks;Caps for water;Cosmetic packaging;pallet;toys;

Behavior Behavior
Melt Flow Rate (190°C/2.16kg)
7.2 g/10 min D 1238
Density
0.959 g/cm³ D 792
Density
0.959 g/cm³ ISO 1183-1
Melt Flow Rate (190°C/2,16 kg)
7.2 g/10 min ISO 1133
More Details
Method
Units
Value
Tensile Strength at Yield (b)
 ISO 527
 MPa
 30
Elongation at Yield (b)
 ISO 527
 %
 9
Tensile Strength at Break (b)
 ISO 527
 MPa
 15
Elongation at Break (b)
 ISO 527
 %
 220
Flexural Modulus Chord 0.05-0.25 % (b)
 ISO 178
 MPa
 1340
Izod Impact Strength 23 °C (b)
 ISO 180
 kJ/m²
 4
Vicat Softening Temperature at 10 N (a)
 ISO 306
 °C
 126
Deflection Temperature Under Load at 0.455 MPa (b)
 ISO 75
 °C
 76
Tensile Strength at Yield (a)
 D 638
 MPa
 29
Elongation at Yield (a)
 D 638
 %
 7.5
Flexural Modulus - 2% Secant (b)
 D 2240
 MPa
 1365
Hardness (c)
 D 2240
 -
 63
Izod Impact Strength (b)
 D 256
 J/m
 35
Deflection Temperature under Load at 0.455 MPa (b)
 D 648
 °C
 74
Vicat Softening Temperature at 10 N (b)
 D 1525
 °C
 126