I'm green bio-basedTM Ethylene Vinyl Acetate Copolymer
SVT2090
SVT2090 is an Ethylene-Vinyl Acetate (EVA) copolymer, developed to meet the needs of the segment of multi-layer packages produced by coextrusion and/or lamination processes. Multilayer structures with SVT2090 can be irradiated to improve physical proprieties, such as adhesion between layers, puncture resistance and hot sealing. Since it presents an exceptional weldability, this product meets the requirements for automatic or semi-automatic lines of cutting, welding and/or packaging (with or without vacuum-packed process). It has excellent performance during extrusion operation, thermal stability, and a low consumption of energy during its processing. It allows production of packages with dimensional uniformity and excellent visual properties. High transparency and gloss enhance the printing and surface finish of the packages.
The minimum biobased content of this grade is 83%, determined according to ASTM D6866.
The minimum biobased content of this grade is 83%, determined according to ASTM D6866.
Process: Coextrusion Films;Film Extrusion - General Use;
Application: Cooled and frozen food packaging;Food packaging;Shrink film.;
Behavior
Melt Flow Rate (190°C/2.16kg)
2.0
g/10 min
ASTM D 1238
Vinyl-Acetate Content
8.5
%
ASTM-D-5594-98
Tensile Strength at Break (MD/TD)
31/24
MPa
D 882
Elongation at Break (MD/TD)
650/1100
%
D 882
More Details
Method
Units
Value
1% Secant Modulus (MD/TD)
D 882
MPa
79/94
2% Secant Modulus (MD/TD)
D 882
MPa
76/79
Dart Drop Impact Strength
D 1709 (B)
gF
175
Elmendorf Tear Strength (MD/TD)
D 1922
gF
200/220
Haze
D 1003
%
3
Gloss - Angle 45º
D 2457
-
90
Density
D 1505 / D 792
g/cm³
0.931
Tensile Strength at Break
D 638
MPa
19
Elongation at Break
D 638
%
700
Hardness
D 2240
Shore A / D
93/45
Melting Point
D 3418
°C
100
Vicat Softening Temperature at 10 N
D 1525
°C
79