Terpolymer
Symbios 4102
Terpolymer
Symbios 4102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on biorented films (BOPP), with heat seal temperature below 120°C on treated face. This product does not have slip and anti-blocking agents so it is indicated for customized formularization. This product is appropriate for metalizing processes.
Symbios 4102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on biorented films (BOPP), with heat seal temperature below 120°C on treated face. This product does not have slip and anti-blocking agents so it is indicated for customized formularization. This product is appropriate for metalizing processes.
Process: BOPP Film;Coextrusion Films;
Application: Coextrusion of Bioriented and Conventional Film;Heat Sealable Bioriented and Conventional Film with Medium Sealing Temperature ;Modifier Properties of Conventional Films;Suitable for use in lamination process.;
Behavior
Nominal Melt Flow (230°C/2.16kg)
5.5
g/10 min
D 1238
Melt Flow Rate (230°C/2.16 kg)
5.5
g/10 min
1133
Secant Modulus 1% (MD/TD)
395/395
MPa
D 882
Tensile Strength at Yield (MD/TD)
18/16
MPa
D 882
More Details
Method
Units
Value
Elongation at Yield (MD/TD)
D 882
%
16/13
Haze
D 1003
%
0.4
Gloss 45°
D 2457
-
96
Sealing Initial Temperature
Braskem Method
°C
115
Density
1183-1
g/cm³
0.902
Flexural Modulus ª
178
MPa
687
Tensile Strength at Yield ª
527-1
MPa
23
Tensile Elongation at Yield ª
527-1
%
13
Rockwell Hardness (R Scale) ª
2039-2
-
73
Notched Izod Impact Strength at 23°C ª
180
kJ/m²
5.5
Notched Charpy Impact Strength at 23°C ª
179
kJ/m²
6.0
Heat Deflection Temperature under Load at 0.455 MPa ª
75-1/75-2
°C
57
Heat Deflection Temperature under Load at 1.820 MPa ª
75-1/75-2
°C
45
Vicat Softening Temperature at 10 N ª
306
°C
121
Density
D 792
g/cm³
0.902
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)
D 790
MPa
700
Tensile Strength at Yield (2 in/min, 50 mm/min)
D 638
MPa
25
Elongation at Yield (2 in/min, 50 mm/min)
D 638
%
13
Rockwell Hardness (R Scale)
D 785
-
73
Notched Izod Impact Strength (at 23°C)
D 256
J/m
55
Notched Izod Impact Strength (at -20°C)
D 256
J/m
20
Heat Deflection Temperature (0.45 Mpa)
D 648
°C
74
Deflection Temperature under Load at 1.820 MPa
D 648
°C
48
Vicat Softening Temperature (at 10 N)
D 1525
°C
121