Terpolymer
Symbios 3102
Terpolymer
Symbios 3102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on cast film coextrusion, with heat seal temperature below 110°C on non-treated face. This product does not have slip and anti-blocking agents so it is indicated for customized formularization. This product is appropriate for metalizing and lamination processes.
Symbios 3102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on cast film coextrusion, with heat seal temperature below 110°C on non-treated face. This product does not have slip and anti-blocking agents so it is indicated for customized formularization. This product is appropriate for metalizing and lamination processes.
Process: Cast Film Extrusion.;Coextrusion Films;
Application: Adequate for Lamination and Metallization Processes;Conventional Sealable Film;Modifier Properties of Conventional Films;Sealing layer for cast film coextrusion;
Behavior
Nominal Melt Flow (230°C/2.16kg)
9.0
g/10 min
D 1238
Melt Flow Rate (230°C/2.16 kg)
9.0
g/10 min
1133
Secant Modulus 1% (MD/TD)
360/410
MPa
D 882
Tensile Strength at Yield (MD/TD)
17/17
MPa
D 882
More Details
Method
Units
Value
Elongation at Yield (MD/TD)
D 882
%
30/13
Haze
D 1003
%
0.3
Gloss 45°
D 2457
-
100
Sealing Initial Temperature
Braskem Method
°C
101
Density
1183-1
g/cm³
0.902
Flexural Modulus ª
178
MPa
670
Tensile Strength at Yield ª
527-1
MPa
22
Tensile Elongation at Yield ª
527-1
%
13
Rockwell Hardness (R Scale) ª
2039-2
-
100
Notched Izod Impact Strength at 23°C ª
180
kJ/m²
5.5
Notched Charpy Impact Strength at 23°C ª
179
kJ/m²
6.5
Heat Deflection Temperature under Load at 0.455 MPa ª
75-1/75-2
°C
57
Heat Deflection Temperature under Load at 1.820 MPa ª
75-1/75-2
°C
44
Vicat Softening Temperature at 10 N ª
306
°C
124
Density
D 792
g/cm³
0.902
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)
D 790
MPa
800
Tensile Strength at Yield (2 in/min, 50 mm/min)
D 638
MPa
26
Elongation at Yield (2 in/min, 50 mm/min)
D 638
%
13
Rockwell Hardness (R Scale)
D 785
-
100
Notched Izod Impact Strength (at 23°C)
D 256
J/m
45
Notched Izod Impact Strength (at -20°C)
D 256
J/m
20
Heat Deflection Temperature (0.45 Mpa)
D 648
°C
79
Deflection Temperature under Load at 1.820 MPa
D 648
°C
49
Vicat Softening Temperature (at 10 N)
D 1525
°C
124