Polypropylene Random Copolymer
Share
Prisma 6410
Prisma 6410 Braskem Logo
Random copolymer

PRISMA® 6410 is a random copolymer of low melt flow, with excellent balance of mechanical properties and high transparency for wall thickness up to 2.0 mm.

Process: Extrusion Blow Molding;

Application: Extrusion-Blow Molding of bottles, housewares, which require high-transparency;

Behavior Behavior
Nominal Melt Flow (230°C/2.16kg)
1.5 g/10 min D 1238
Melt Flow Rate (230°C/2.16 kg)
1.5 g/10 min 1133
Density
0.902 g/cm³ 1183-1
Flexural Modulus ª
800 MPa 178
More Details
Method
Units
Value
Tensile Strength at Yield ª
 527-1
 MPa
 25
Tensile Elongation at Yield ª
 527-1
 %
 14
Notched Izod Impact Strength at 23°C ª
 180
 kJ/m²
 22
Notched Charpy Impact Strength at 23°C ª
 179
 kJ/m²
 21
Heat Deflection Temperature under Load at 0.455 MPa ª
 75-1/75-2
 °C
 63
Heat Deflection Temperature under Load at 1.820 MPa ª
 75-1/75-2
 °C
 46
Density
 D 792
 g/cm³
 0.902
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)
 D 790
 MPa
 900
Tensile Strength at Yield (2 in/min, 50 mm/min)
 D 638
 MPa
 26
Elongation at Yield (2 in/min, 50 mm/min)
 D 638
 %
 14
Notched Izod Impact Strength (at 23°C)
 D 256
 J/m
 350
Heat Deflection Temperature (0.45 Mpa)
 D 648
 °C
 70
Haze (20 mil, 0.5 mm injection molded plaque)
 1003
 %
 12