Polypropylene Random Copolymer
Share
Prisma 1410
Prisma 1410 Braskem Logo
Random copolymer

Prisma 1410 is a high melt flow rate random copolymer, designed for injection moulding. This product exhibits exceptional transparency, very good stiffness/impact strength balance and excellent processability.
 

Process: Injection molding;

Application: High transparency parts with an excellent balance stiffness / impact;

Behavior Behavior
Nominal Melt Flow (230°C/2.16kg)
40 g/10 min D 1238
Melt Flow Rate (230°C/2.16 kg)
40 g/10 min 1133
Density
0.902 g/cm³ 1183-1
Flexural Modulus ª
1050 MPa 178
More Details
Method
Units
Value
Tensile Strength at Yield ª
 527-1
 MPa
 28
Tensile Elongation at Yield ª
 527-1
 %
 14
Rockwell Hardness (R Scale) ª
 2039-2
 -
 80
Notched Izod Impact Strength at 23°C ª
 180
 kJ/m²
 2.8
Notched Izod Impact Strength at -20°C ª
 180
 kJ/m²
 1.3
Heat Deflection Temperature under Load at 0.455 MPa ª
 75-1/75-2
 °C
 82
Heat Deflection Temperature under Load at 1.820 MPa ª
 75-1/75-2
 °C
 50
Vicat Softening Temperature at 10 N ª
 306
 °C
 129
Haze ª
 13468-1
 %
 8
Density
 D 792
 g/cm³
 0.902
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)
 D 790
 MPa
 1000
Tensile Strength at Yield (2 in/min, 50 mm/min)
 D 638
 MPa
 29
Elongation at Yield (2 in/min, 50 mm/min)
 D 638
 %
 14
Rockwell Hardness (R Scale)
 D 785
 -
 79
Notched Izod Impact Strength (at 23°C)
 D 256
 J/m
 50
Notched Izod Impact Strength (at -20°C)
 D 256
 J/m
 15
Heat Deflection Temperature (0.45 Mpa)
 D 648
 °C
 81
Deflection Temperature under Load at 1.820 MPa
 D 648
 °C
 50
Vicat Softening Temperature (at 10 N)
 D 1525
 °C
 129
Haze (20 mil, 0.5 mm injection molded plaque)
 1003
 %
 8