Polypropylene Homopolymer
Share
PH 0952
PH 0952 Braskem Logo
Homopolymer

PH 0952 is a medium melt flow rate homopolymer, with slip and antiblocking agents. This product is designed for technical films segment and packaging for cast and blown film extrusion. This product features excellent optical properties and good processability.

Process: Blown Film Extrusion;Cast Film Extrusion.;

Application: Films for lamination;Food packaging;roll films for automatic packaging;Textile Applications;Very thin film on high-speed line, low thickness.;

Behavior Behavior
Nominal Melt Flow (230°C/2.16kg)
8.0 g/10 min D 1238
Melt Flow Rate (230°C/2.16 kg)
8.0 g/10 min 1133
Secant Modulus 1% (MD/TD)
600/620 MPa D 882
Tensile Strength at Yield (MD/TD)
23/23 MPa D 882
More Details
Method
Units
Value
Elongation at Yield (MD/TD)
 D 882
 %
 11/10
Haze
 D 1003
 %
 2.5
Gloss 45°
 D 2457
 -
 93
Sealing Initial Temperature
 Braskem Method
 ºC
 115
Secant Modulus 1% (MD/TD)
 D 882
 MPa
 560/560
Tensile Strength at Yield (MD/TD)
 D 882
 MPa
 23/23
Elongation at Yield (MD/TD)
 D 882
 %
 12/11
Haze
 D 1003
 %
 2.0
Gloss 45°
 D 2457
 -
 92
Sealing Initial Temperature
 Braskem Method
 ºC
 118
Density
 1183-1
 g/cm³
 0.905
Flexural Modulus ª
 178
 MPa
 1300
Tensile Strength at Yield ª
 527-1
 MPa
 35
Tensile Elongation at Yield ª
 527-1
 %
 11
Rockwell Hardness (R Scale) ª
 2039-2
 -
 90
Notched Izod Impact Strength at 23°C ª
 180
 kJ/m²
 3.7
Heat Deflection Temperature under Load at 0.455 MPa ª
 75-1/75-2
 °C
 95
Heat Deflection Temperature under Load at 1.820 MPa ª
 75-1/75-2
 °C
 55
Vicat Softening Temperature at 10 N ª
 306
 °C
 149
Density
 D 792
 g/cm³
 0.905
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)
 D 790
 MPa
 1200
Tensile Strength at Yield (2 in/min, 50 mm/min)
 D 638
 MPa
 35
Elongation at Yield (2 in/min, 50 mm/min)
 D 638
 %
 11
Rockwell Hardness (R Scale)
 D 785
 -
 90
Notched Izod Impact Strength (at 23°C)
 D 256
 J/m
 30
Heat Deflection Temperature (0.45 Mpa)
 D 648
 °C
 95
Deflection Temperature under Load at 1.820 MPa
 D 648
 °C
 55
Vicat Softening Temperature (at 10 N)
 D 1525
 °C
 149