Polypropylene Homopolymer
Share
PH 0130
PH 0130 Braskem Logo
Homopolymer

PH 0130 is a low melt flow rate additivated homopolymer used for general purposes. This resin is designed for blow moulding and extrusion. PH 0130 features excellent processability and stiffness/impact strength balance.

Process: Extrusion Blow Molding;General extrusion.;

Application: Bottles for mineral water, juices, cosmetics and general uses;Flat and corrugated sheets;Profiles;Ropes;Tapes in general;Tear tape;

Behavior Behavior
Nominal Melt Flow (230°C/2.16kg)
1.2 g/10 min D 1238
Melt Flow Rate (230°C/2.16 kg)
1.2 g/10 min 1133
Density
0.905 g/cm³ 1183-1
Flexural Modulus ª
1350 MPa 178
More Details
Method
Units
Value
Tensile Strength at Yield ª
 527-1
 MPa
 36
Tensile Elongation at Yield ª
 527-1
 %
 10
Rockwell Hardness (R Scale) ª
 2039-2
 -
 98
Notched Izod Impact Strength at 23°C ª
 180
 kJ/m²
 4.7
Heat Deflection Temperature under Load at 0.455 MPa ª
 75-1/75-2
 °C
 92
Vicat Softening Temperature at 10 N ª
 306
 °C
 156
Density
 D 792
 g/cm³
 0.905
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)
 D 790
 MPa
 1300
Tensile Strength at Yield (2 in/min, 50 mm/min)
 D 638
 MPa
 36
Elongation at Yield (2 in/min, 50 mm/min)
 D 638
 %
 10
Rockwell Hardness (R Scale)
 D 785
 -
 98
Notched Izod Impact Strength (at 23°C)
 D 256
 J/m
 45
Heat Deflection Temperature (0.45 Mpa)
 D 648
 °C
 92
Vicat Softening Temperature (at 10 N)
 D 1525
 °C
 156