PROXESS
PROXESS1809
Melt Flow Rate (190°C/2.16kg)
D 1238
0.90 g/10 min
Density
D 792
0.918 g/cm³
Tensile Strength at Break (MD/TD)
D 882
40/30 MPa
Elongation at Break (MD/TD)
D 882
770/930 %
PROXESS
PROXESS2606
Melt Flow Rate (190°C/2.16kg)
D 1238
0.6 g/10 min
Density
D 792
0.926 g/cm³
Tensile Strength at Break (MD/TD)
D 882
40/30 MPa
Elongation at Break (MD/TD)
D 882
1020/1090 %
PROXESS
PROXESS 1806S3
Melt Flow Rate (190°C/2.16kg)
D 1238
0.6 g/10 min
Density
D 792
0.918 g/cm³
Tensile Strength at Break (MD/TD)
D 882
30/20 MPa
Elongation at Break (MD/TD)
D 882
620/850 %
PROXESS
PROXESS1509XP
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.9 g/10 min
Density
ASTM D 792
0.916 g/cm³
Tensile Strength at Break (MD/TD)
D 882
27/20 MPa
Elongation at Break (MD/TD)
D 882
640/760 %
PROXESS
PROXESS 3310
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
1 g/10 min
Density
ASTM D 792
0.933 g/cm³
Tensile Strength at Break (MD/TD)
D 882
50/40 MPa
Elongation at Break (MD/TD)
D 882
980/1300 %
Recycled
RPL 0C1 WE
.jpg)
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.5 g/10 min
Density
ASTM D 792
0.925 g/cm³
Tensile Strength at Break (MD/TD)
D 882
24/23 MPa
Tensile Strength at Yield (MD/TD)
D 882
09/11 MPa
Recycled
RPL 0C1 BE
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.5 g/10 min
Density
ASTM D 792
0.925 g/cm³
Tensile Strength at Break (MD/TD)
D 882
24/23 MPa
Tensile Strength at Yield (MD/TD)
D 882
09/11 MPa
Recycled
RGR 7A2 WE
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.27 g/10 min
Melt Flow Rate (190°C/21.6kg)
ASTM D 1238
26 g/10 min
Density
ASTM D 792
0.962 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
1100 MPa
Recycled
RPR 7A2 WE
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.40 g/10 min
Melt Flow Rate (190°C/21.6kg)
ASTM D 1238
0.34 g/10 min
Density
ASTM D 792
> 0.955 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
1100 MPa
Recycled
DA065A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.21 g/10 min
Melt Flow Rate (190°C/21.6kg)
ASTM D 1238
24 g/10 min
Density
ASTM D 792
0.968 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
950 MPa
Recycled
WCL L004 SCB
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.4 g/10 min
Density
ASTM D 792
0.949 g/cm³
Tensile Strength at Break (MD/TD)
D 882
24/23 MPa
Tensile Strength at Yield (MD/TD)
D 882
09/11 MPa
Recycled
WCL L004 SCT
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.4 g/10 min
Density
ASTM D 792
0.925 g/cm³
Tensile Strength at Break (MD/TD)
D 882
24/23 MPa
Tensile Strength at Yield (MD/TD)
D 882
09/11 MPa
Recycled
DL085A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
2.62 g/10 min
Melt Flow Rate (190°C/21.6kg)
ASTM D 1238
56.34 g/10 min
Density
ASTM D 792
0.921 g/cm³
Recycled
DA054B
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.3 g/10 min
Melt Flow Rate (190°C/21.6kg)
ASTM D 1238
28 g/10 min
Density
ASTM D 792
0.955 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
1050 MPa
Recycled
RPL 4C5 WE
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
1.5 g/10 min
Density
ASTM D 792
0.925 g/cm³
Tensile Strength at Break (MD/TD)
ASTM D 882
29/28 MPa
Elongation at Yield (MD/TD)
ASTM D 882
1090/1350 %
Recycled
RPL 4C2 BL
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
1.5 g/10 min
Density
ASTM D 792
0.925 g/cm³
Tensile Strength at Break (MD/TD)
ASTM D 882
29/28 MPa
Elongation at Break (MD/TD)
ASTM D 882
1100/1370 %
Recycled
DA 073A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
1.5 g/10 min
Density
ASTM D 792
0.955 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
1050 MPa
Izod Impact Strength (b)
ASTM D 256
25 J/m
Recycled
DL085C
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
2.4 g/10 min
Melt Flow Rate (190°C/21.6kg)
ASTM D 1238
56.34 g/10 min
Density
ASTM D 792
0.921 g/cm³
Recycled
DLR 003A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.85 g/10 min
Density
ASTM D 792
0.941 g/cm³
Recycled
DAR001A
Melt Flow Rate (190°C/5kg)
ASTM D 1238
0.55 g/10 min
Density
ASTM D 792
0.968 g/cm³
Recycled
DA 074A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
1.5 g/10 min
Density
ASTM D 792
0.955 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
1150 MPa
Izod Impact Strength (b)
ASTM D 256
25 J/m
Recycled
DA 061A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
7 g/10 min
Density
ASTM D 792
0.95 g/cm³
Recycled
DLR 001A
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
0.55 g/10 min
Density
ASTM D 792
0.93 g/cm³
Recycled
RPR 5C4 BK
Melt Flow Rate (190°C/2.16kg)
ASTM D 1238
1.5 g/10 min
Density
ASTM D 792
0.955 g/cm³
Flexural Modulus - 2% Secant (b)
ASTM D 790
1150 MPa
Izod Impact Strength (b)
ASTM D 256
25 J/m
de 1